For the material performance requirements of mold manufacturing, the details are as follows:
The spheroidizing annealing temperature range is wide, the annealing hardness is low, the fluctuation range is small, and the spheroidization rate is high.
It has low hot forging deformation resistance, good plasticity, wide forging temperature range, low tendency for forging cracking and precipitation of reticulated carbides.
3. Oxidation and decarburization sensitivity
When heated at high temperature, the anti-oxidation energy is good, the decarburization speed is slow, and it is not sensitive to the heating medium, and the tendency to produce pitting is small.
Large cutting amount, low tool loss and low surface roughness.
Uniform and high surface hardness after quenching.
After quenching, a deep hardened layer can be obtained, which can be hardened with a mild quenching medium.
The relative loss of the grinding wheel is small, the maximum amount of grinding without the burn is large, and it is not sensitive to the quality of the grinding wheel and the cooling condition, and it is not easy to cause abrasion and grinding crack.
8. Quenching deformation cracking tendency
The conventional quenching volume change is small, the shape is warped, the distortion is slight, and the abnormal deformation tendency is low. Conventional quenching cracking has low sensitivity and is not sensitive to quenching temperature and workpiece shape.